Resoltech 1020T Thixotropic Hand Lay-Up Epoxy Resin

RESOLTECH 1020T is a pregel wood adhesive system optimised for the manufacture of laminated wood parts and structures. It provides ease of use, low toxicity to the user, good impregnation of the timber surface, high mechanical performance of the cured structure and an adjustable working time. 1020T makes bonds that are stronger than the timber itself, enhancing its mechanical properties and producing long lasting heavy duty structures for marine, building and engineering applications.

Mixing ratio by weight: 100 / 30

Mixing ratio by volumen: 3 / 1

Variable gel time depending on hardener.

Maximum Tg depending on hardener: 51 - 60.3 ºC.

Colour: Transparent yellowish

Type of supply

Resoltech 1020T (1 kg) + 1028S (0,3 kg), gel time of 22 min for 70 g at 23 ºC

Resoltech 1020T (5 kg) + 1028S (1,5 kg), gel time 22 min for 70 g at 23 ºC

Resoltech 1020T (25 kg) + 1028S (7,5 kg),  gel time of22 min for 70 g at 23 ºC

Resoltech 1020T (1 kg) + 1026S (0,3 kg), gel time of 40 min for 70 g at 23 ºC

Resoltech 1020T (5 kg) + 1026S (1,5 kg), gel time of 40 min for 70 g at 23 ºC

Resoltech 1020T (25 kg) + 1026S (7,5 kg), gel time of 40 min for 70 g at 23 ºC

Resoltech 1020T (1 kg) + 1025S (0,3 kg), gel time of 1 h 15 min for 70 g at 23 ºC

Resoltech 1020T (5 kg) + 1025S (1,5 kg), gel time of 1h 15 min for 70 g at 23 ºC

Resoltech 1020T (25 kg) + 1025S (7,5 kg), gel time of 1 h 15 min for 70 g at 23 ºC

Resoltech 1020T (1 kg) + 1024S (0,3 kg), gel time of 3 h 10 min for 70 g at 23 ºC

Resoltech 1020T (5 kg) + 1024S (1,5 kg), gel time of 3 h 10 min for 70 g at 23 ºC

Resoltech 1020T (25 kg) + 1024S x (7,5 kg), gel time of 3 h 10 min for 70 g at 23 ºC

Resoltech 1020T (1 kg) + 1023S (0,3 kg), gel time of 9 h 20 min for 70 g at 23ºC

Resoltech 1020T (5 kg) + 1023S (1,5 kg), gel time of 9 h 20 min for 70 g at 23ºC

Resoltech 1020T (25 kg) + 1023S (7,5 kg), gel time of 9 h 20 min for 70 g at 23 ºC