Carbon Fibre Sheet 1000mm x 500mm x 1mm

Carbon fibre sheet laminated with prepreg technology.

The top and bottom layer always have an attractive carbon "look" (twill weave). The carbon fibres are placed in the core in the longitudinal and transverse directions, providing the sheets with optimal strength and stiffness.

It is necessary to protect the surface with a UV protection coating if it is to be exposed to sunlight.

Main Features

General Properties

• Length: 1000 ±4 mm
• Width: 500 ±4 mm
• Thickness: 1 ±0.2 mm
• Section: 0.005 m²
• Weight: 840 g
• Density: 1600 kg/m³
• Finish: Semi-gloss, twill on both sides

Mechanical Strengths according to UNI EN 13706-1-2-3 ISO527

• Fibre direction: 50% UD-0º / 50% UD-90º
• Elastic Modulus (E): 70 GPa
• Elastic Modulus x section (E A):
• Tensile Strength > of 468 MPa
• Specific stiffness: 44 MN m/kg
• Maximum flexural stress: 1804 MPa
• Flexural stiffness: 4.17x10³ MPa
• Tensile strength in section:

Material Properties

• Fibre type: T300 or equivalent, 3K
• Resin type: Epoxy
• Tg: 80 ºC

Other Characteristics

• Carbon fibre content by volume (Vf): 69%
• Glass transition temperature (Tg), ISO 11357-2 DSC: 80 ºC
• Recommended service temperature:

Caution: pultruded carbon fibre materials are electrically conductive. If the material has been packaged, be careful when removing/unrolling the film as the material may be under tension.

When machining (cutting, sanding, drilling...), it is recommended to wear protective masks, goggles, and gloves.